F. Güell, J.O. Ossó, A.R. Goñic, A. Cornet and J.R. Morante

Superlattices and Microstructures, Volume 45, Issues 4-5, April-May 2009, Pages 271-276, doi:10.1016/j.spmi.2008.10.030

superlat-micorstr-cover

Single crystal ZnO nanowires with lengths and diameters ranging from 2 to 30 μm and 100 to 300 nm, respectively, have been grown by the vapor transport method on SiO2/Si substrates using Au as catalyst. Their Raman and emission properties under different excitation wavelengths have been studied at the nanoscale. Whereas Raman measurements on nanowires corroborate the well-known ZnO phonon characteristics, their photoluminescence spectra exhibit a very broad emission band, mainly in the visible region from 450 to 800 nm, which corresponds to different defect-related recombination processes. Spectrally resolved scanning near-field optical microscopy, SNOM, of single ZnO nanowires have also been performed for a direct imaging of the photoluminescence emission with high spatial resolution below 100 nm, establishing a relationship with the simultaneously acquired topography.